1% nickel deposit. Used in applications where low temperature notch toughness is required. Can be used on weathering types of steel where color match is not required.

Description

Welding Positions

Flux Cored Welding Wire

Classification:

A5.29: E80T1-Ni1CJ H8/-Ni1MJ H8

TYPICAL DIFFUSIBLE HYDROGEN*

Slow-freezing, rutile type, flux-cored wire

100% Carbon Dioxide (CO2), 75-80% Argon (Ar)/Balance Carbon Dioxide (CO2) 35-50 cfh, (17-24 l/min)

Direct Current Electrode Positive (DCEP)

5/64” (2.0 mm), 3/32” (2.4 mm)

Not recommended

Product should be stored in a dry, enclosed environment, and in its original intact packaging

Single or multiple pass applications with 100% CO2 or 75-80Ar/20-25CO2 shielding gas

• Single or multi-pass welding

• High-Strength Low-Alloy steels

• Structural and bridge fabrication
• Heavy equipment

• Weathering steels

• Storage and pressure vessels

APPLICATIONS

SLAG SYSTEM OR WIRE TYPE

SHIELDING GAS

TYPE OF CURRENT

STANDARD DIAMETERS

RE-DRYING

TYPICAL WELD METAL CHEMISTRY* (Chem Pad)

TYPICAL MECHANICAL PROPERTIES* (As Welded)

CONFORMANCES AND APPROVALS:

• AWS A5.20, E80T1-Ni1CJ H8, E80T1-Ni1MJ H8
• AWS A5.20M, E550T1-Ni1CJ H8, E550T1-Ni1MJ H8
• ASME SFA 5.20, E80T1-Ni1CJ H8, E80T1-Ni1MJ H8
• ABS, 100% CO2, E80T1-Ni1CJ H8, (5/64” - 3/32” diameter electrodes)

• CWB, 100% CO2, E550T1-Ni1C-H8 (E80T1-NiC H8)

• Maintaining a proper welding procedure - including pre-heat and interpass temperatures - may be critical
depending on the type and thickness of steel being welded.
• See Above: This information was determined by welding using 100% CO2 shielding gas with a flow rate between
35-50 cfh (17-24 l/min). When using 75-80% Argon (Ar)/ Balance CO2 shielding gases, reduce voltage by approximately 1 volt.

STORAGE

FEATURES AND BENEFITS

• Tubular wire deposit chemistry comparable to that of E8018-C3 stick electrodes
• Performance optimized for flat and horizontal welding 
• Excellent low-temperature impact toughness
• “H8” low-hydrogen weld deposit

• Provides premium arc characteristics AND mechanical properties 

• Suitable for similar applications to E8018-C3 electrodes, and capable of a large productivity improvement

• Improved operator appeal in flat and horizontal positions compared to all-position wires/electrodes

• Helps minimize risk of cracking in critical applications

• Helps minimize risk of hydrogen-induced cracking

• Assists maintaining high production without sacrificing weld integrity

Keywords

AWS A5.29: E80T1-Ni1CJ H8/-Ni1MJ H8,Flux Cored Welding Wire ,China, Tianjin.

STANDARD DIAMETERS AND PACKAGES: 

For a complete list of diameters and packaging, please contact Hobart Brothers at (800) 424-1543 or (937) 332-5188 for International Customer Service.

TYPICAL CHARPY V-NOTCH IMPACT VALUES* (As Welded)