Produces weld metal with a minimum of 100 ksi tensile strength. It has excellent low temperature toughness to -60F.
Description
Welding Positions
Flux Cored Welding Wire
Classification:
AWS A5.28: E100C-K3
Gas-shielded, metal-powder, metal-cored wire


75-95% Argon (Ar)/Balance Carbon Dioxide (CO2), 35-50 cfh (17-24 /min)



 Direct Current Electrode Positive (DCEP)





0.045”(1.2 mm), 0.052”(1.4 mm)


Not recommended



 Product should be stored in a dry, enclosed environment, and in its original intact packaging
Single and multiple pass applications with a Argon/CO2 shielding gas


●Single or multi-pass welding
●High-Strength Low-Alloy Steels
●HY-80 Steel
●ASTM A514 (>2" Thickness)
●Heavy equipment
●Shipbuilding
APPLICATIONS
SHIELDING GAS
TYPE OF CURRENT
STANDARD DIAMETERS
RE-DRYING
TYPICAL WELD METAL CHEMISTRY* (Chem Pad)
CONFORMANCES AND APPROVALS
●AWS A5.28, E100C-K3 H4
●AWS A5.28M, E69C-K3 H4
●ASME SFA 5.28, E100C-K3 H4
STANDARD DIAMETERS AND PACKAGES: 
For a complete list of diameters and packaging, please contact
●Maintaining a proper welding procedure - including pre-heat and interpass temperatures - may be critical
depending on the type and thickness of steel being welded.
●Pulse waveforms are designed with nominal operating points that may result in average voltage and current
values that differ from the above table. Generally, pulse processes can be expected to produce lower heat
inputs than a standard CV process.
●For out of position welding, short circuit or pulsed spray transfer mode must be used.
●See Above: This information was determined by welding using 75% Ar/25% CO2 shielding gas with a flow rate between 35-50 cfh (17-24 /min). For the lower CO2 shielding gas mixtures within the recommended range, reduce listed voltages by 1-3 volts.
●All positions include: Flat, Horizontal, Vertical Up, and Overhead.
STORAGE
FEATURES AND BENEFITS
●●Metal-cored wire provides higher deposition rate than solid wire electrodes
●Excellent low-temperature toughness
●All-position capable using short-circuit or pulsed-spray transfers
●High-strength deposit


●Helps increase travel speed and improve productivity
●Helps minimize risk of cracking in critical applications
●Provides versatility; minimizes the need for multiple wires
●Suitable for use on a wide range of high-strength low-alloy materials
INDUSTRIES
Railcar, Automotive, General Fabrication
WIRE TYPE
TYPICAL MECHANICAL PROPERTIES* (As Welded)
TYPICAL CHARPY V-NOTCH IMPACT VALUES* (As Welded)