Agglomerated and active flux (with Cr-compensating & Ni / Mo alloying characteristic) designed for hardfacing, overlay stripwelding and joint cladding together with stainless strip electrodes of the Cr–, CrNi(Mo)–steel types. Applicable for SAW–process as well as for use with the ESO® (Extended Stick Out)–cladding system which enables highest possible deposit rates as a result of the Joule heat (I2R)–effect.EN 760: SA CS 3 NiMo DC gives excellent slag removal without slag residuals, in the 1st layer on preheated substrates as well as in subsequent layers. The flux has low hydrogen potential, which makes it most suitable for overlay welding of heat resistant steels such as A387–types. Smooth weld bead appearance and notch–free transitions are features achievable with all cladding processes. Constant dilution rates can be gained when using process–characteristic welding parameters. EN 760: SA CS 3 NiMo DC shows constant chemical reactions as typical for a BAVARIA – alloyed flux.

Classification:

ISO 14174: S A CS 3 5654 DC(EN 760: SA CS 3 NiMo DC)

Characteristics 

Characteristic chemical constituents

Welding Positions:

Flux density: 1.0 – 1.1 kg / dm³ (l)
Grain size acc. to ISO 14174: 2 – 20 ( Tyler 8 x 65)

Welding Flux

Application

EN 760: SA CS 3 NiMo DC can be used for hardfacing, joint cladding and surfacing. In combination with appropriate strip electrodes of the EQ300/EQ400 (without Nb) series according to A5.9 or according to EN ISO 14343 (EN 12072) constant weld overlays are achievable. The flux is highly viscouse and creates a reinforce-effect for the weld pool. This characteristic brings exceptional advantages by cladding low diameter-rolls.

Flux type:

Calcium-Silicate